Characteristics of Al2O3/native oxide/n-GaN capacitors by post-metallization annealing. (31st January 2019)

• Record Type: Journal Article
• Authors: Yuge, Kazuya; Nabatame, Toshihide; Irokawa, Yoshihiro; Ohi, Akihiko; Ikeda, Naoki; Sang, Liwen; Koide, Yasuo; Ohishi, Tomoji
• Is Part Of: Semiconductor science and technology. Volume 34:Number 3(2019)
• Publication Date: 2019-01-31
• Subjects: GaN -- Al2O3 dielectric -- native oxide interlayer -- flatband voltage -- fixed charge -- ALD; Semiconductors -- Periodicals; 621.38152
• DOI: 10.1088/1361-6641/aafdbd
• Languages: English
• ISSNs: 0268-1242

Abstract

Abstract: This work investigated characteristics of Al2 O3 /native oxide/n-GaN MOS capacitors by post-metallization annealing (PMA). A native oxide interlayer which composed of ε - and γ -Ga2 O3 phases (Native oxide) and the reduced amount of one (Reduced) on n-GaN were prepared by cleaning only a sulfuric acid peroxide mixture (SPM) and both SPM and buffered hydrofluoric acid, respectively. The effect of trimethylaluminum precursor on removal of a native oxide layer was not observed during Al2 O3 deposition using atomic layer deposition. An as-grown capacitor (Native oxide) exhibited a small flatband voltage ( V fb ) hysteresis of ∼30 mV and a large frequency dispersion, suggesting that the initial growth of the Al2 O3 resulted in the formation of electrical defects on the GaN surface. Both the V fb hysteresis and frequency dispersion were drastically improved by PMA of the device at 300 °C. The positive fixed charge values ( Q IL ) estimated from the relationships between capacitance equivalent thickness and V fb were +6.1 × 10 12 and +0.4–1.0 × 10 12 cm −2 for as-grown and PMA-processed capacitors in the PMA temperature range of 300 °C–600 °C, respectively. The interface state density ( D it ) determined using a conductance method was also significantly reduced (by an order of magnitude) after PMA processing at 300 °C. These trends in the Q IL and D it data were observed in both the Native oxide and Reduced capacitors, indicating that this interlayer does not greatly affect fixed charge generation at the Al2 O3 /native oxide and Al2 O3 /modified native oxide interfaces. As a result, two types of treatments result in insignificant difference in the electrical properties of the capacitors.