Synthesis of nickel–zinc–yttrium ferrites: Structural elucidation and dielectric behavior evaluation. (January 2016)

• Record Type: Journal Article
• Authors: Ishaque, M.; Khan, Muhammad Azhar; Ali, Irshad; Athair, Muhammad; Khan, Hasan M.; Asif Iqbal, M.; Islam, M.U.; Warsi, Muhammad Farooq
• Is Part Of: Materials science in semiconductor processing. Volume 41(2016:Jan.)
• Page Start: 508
• Page End: 512
• Publication Date: 2016-01
• Subjects: XRD -- FTIR -- SEM -- Electrical resistivity -- Dielectric parameters; Semiconductors -- Periodicals; Integrated circuits -- Materials -- Periodicals; Semiconducteurs -- Périodiques; Circuits intégrés -- Matériaux -- Périodiques; Electronic journals; 621.38152
• DOI: 10.1016/j.mssp.2015.10.028
• Languages: English
• ISSNs: 1369-8001

Abstract

Abstract: Novel Ni0.6 Zn0.4 Y2 x Fe2−2 x O4 soft spinel ferrites were prepared via double sintering ceramic route. The influence of Y 3+ cations on structural, morphological, electrical and dielectric properties was investigated. X-ray diffraction (XRD) confirmed the formation of single phase spinel structure for 0≤ x ≤0.06 and thereafter a small peak of orthorhombic phase (FeYO3 ) appeared for x >0.06. The incorporation of yttrium altered the lattice constant. The variation in lattice constant with respect to the Y 3+ contents was non-linear. The variation of lattice constant may be attributed to larger ionic radius of Y 3+ as compare to Fe 3+ cations and solubility limit of substituted cations. Fourier transform infrared (FTIR) spectra showed two strong absorption bands around 600 cm −1 and 400 cm −1 which confirmed the spinel structure. The dc electrical resistivity was found to increase from 5.67×10 5 to 8.48×10 8 Ω cm with the increased Y 3+ contents. The dielectric constant and dielectric loss tangent were significantly impeded by increasing the yttrium contents. The optimized electrical resistivity and reduced dielectric parameters suggest the possible use of these ferrites in the fabrication of microwave devices.