Investigations on effect of pore architectures of additively manufactured novel hydroxyapatite coated PLA/Al2O3 composite scaffold for bone tissue engineering. Issue 5 (10th January 2023)

• Record Type: Journal Article
• Authors: Choudhary, Neha; Ghosh, Chandrachur; Sharma, Varun; Roy, Partha; Kumar, Pradeep
• Is Part Of: Rapid prototyping journal. Volume 29:Issue 5(2023)
• Page Start: 1061
• Page End: 1079
• Publication Date: 2023-01-10
• Subjects: Additive manufacturing -- Scaffolds -- Composites -- Alumina -- Hydroxyapatite -- Ceramics; Engineering design -- Periodicals; 620.004205
• DOI: 10.1108/RPJ-09-2022-0303
• Languages: English
• ISSNs: 1355-2546

Abstract

Abstract : Purpose: The purpose of this paper is to fabricate the scaffolds with different pore architectures using additive manufacturing and analyze its mechanical and biological properties for bone tissue engineering applications. Design/methodology/approach: The polylactic acid (PLA)/composite filament were fabricated through single screw extrusion and scaffolds were printed with four different pore architectures, i.e. circle, square, triangle and parallelogram with fused deposition modelling. Afterwards, scaffolds were coated with hydroxyapatite (HA) using dip coating technique. Various physical and thermo-mechanical tests have been conducted to confirm the feasibility. Furthermore, the biological tests were conducted with MG63 fibroblast cell lines to investigate the biocompatibility of the developed scaffolds. Findings: The scaffolds were successfully printed with different pore architectures. The pore size of the scaffolds was found to be nearly 1, 500 µm, and porosity varied between 53% and 63%. The fabricated circular pore architecture resulted in highest average compression strength of 13.7 MPa and modulus of 525 MPa. The characterizations showed the fidelity of the work. After seven days of cell culture, it was observed that the developed composites were non-toxic and supported cellular activities. The coating of HA made the scaffolds bioactive, showing higher wettability, degradation and high cellular responses. Originality/value: The research attempts highlight the development of novel biodegradable and biocompatible polymer (PLA)/bioactive ceramic (Al2 O3 ) composite for additive manufacturing with application in the tissue engineering field.