Investigation of in-situ tribological performance of Polyimide-MoS2/PTFE composite under atomic oxygen irradiation. (May 2023)

• Record Type: Journal Article
• Authors: Hu, Hanjun; He, Ying; Wang, Qihua; Tao, Liming
• Is Part Of: Tribology international. Volume 183(2023)
• Publication Date: 2023-05
• Subjects: In-situ -- PI-MoS2/PTFE -- AO irradiation -- Tribology; Tribology -- Periodicals; 621.89
• DOI: 10.1016/j.triboint.2023.108437
• Languages: English
• ISSNs: 0301-679X

Abstract

Abstract: Polyimide (PI)-MoS2 /PTFE composite was fabricated and its tribological properties were investigated under different conditions, i.e., vacuum, ex-situ AO irradiation and in-situ AO irradiation. The friction pair was 400 C ball on the disk of this composite. By using SEM, AFM, XPS and angle-resolved XPS, the characterizations of morphology, topography and chemical components at the sliding interface were studied comprehensively. Because the effects were just limited into the very top surface, the ex-situ AO irradiation didn't deteriorate the tribological properties. Nevertheless, in-situ AO irradiation persistently interfered the formation of shear layer at the track and transfer film at the scar as the sliding was proceeded, which resulted in severe deterioration of the tribological performance. It was determined there were negative synergistic effects between friction and AO irradiation, which suggested in-situ friction under AO environment was more scientific and practical for the investigation of exposed lubricants in LEO. Highlights: Friction behaviours of PI-MoS2/PTFE composite was investigated by a combination of a vacuum tribometer and an AO irradiation device. A strong negative synergistic effect on the tribological interface from the friction and AO irradiation.