Highly transparent cubic γ-Al2O3 ceramic prepared by high-pressure sintering of home-made nanopowders. Issue 9 (August 2023) - Chen, Xingtao
Abstract: Highly transparent gamma-aluminum oxide (γ-Al2 O3 ) ceramics were fabricated for the first time, by combining homogeneous precipitation and high-pressure sintering in the absence of exogenous dopants. The resulting cubic γ-Al2 O3 transparent ceramic material exhibits a promising replacement for single-crystal sapphire. The optimum optical properties are achieved in response to sintering at 5 GPa and a temperature of 300 °C and include maximum transmittance of 86% in the range of 0.6–1.2 µm which are properties that are comparable to those of single-crystal sapphire (∼86%). Vickers hardness (16 GPa) and compressive strength (350 MPa) in response to high-pressure sintering are also similar to those of a conventional sapphire single crystal. Meanwhile, the dielectric constant (9.46) is comparable to that of sapphire in the C-axis direction. These findings will facilitate further development of transparent Al2 O3 ceramics for use in a wider range of optical applications.