Mortars with alkali-activated municipal solid waste incinerator bottom ash and fine recycled aggregates. (20th March 2021)

• Record Type: Journal Article
• Authors: Casanova, S.; Silva, R.V.; de Brito, J.; Pereira, M.F.C.
• Is Part Of: Journal of cleaner production. Volume 289(2021)
• Publication Date: 2021-03-20
• Subjects: Municipal solid waste -- Incinerator bottom ash -- Alkali-activated materials -- Recycled aggregates -- Curing conditions; Factory and trade waste -- Management -- Periodicals; Manufactures -- Environmental aspects -- Periodicals; Déchets industriels -- Gestion -- Périodiques; Usines -- Aspect de l'environnement -- Périodiques; 628.5
• DOI: 10.1016/j.jclepro.2020.125707
• Languages: English
• ISSNs: 0959-6526

Abstract

Abstract: Milled municipal solid waste incinerator bottom ash was used as a precursor in the production of alkali-activated mortars with recycled concrete aggregates as a sand substitute. Fly ash was used as control precursor and sodium hydroxide as an alkaline activator. Different thermal curing regimens were used: 24 h in ambient conditions; 24 h/70 °C; 48 h/70 °C; and 24 h/90 °C. Mechanical and durability-related performances were evaluated (i.e. flexural and compressive strength, modulus of elasticity, ultrasonic pulse velocity, carbonation, capillary water absorption, and shrinkage). The reaction between metallic aluminium from municipal solid waste incinerator bottom ash and OH − ions produced hydrogen gas, causing expansion, porosity increase and thus decline in performance. Low stability in high relative humidity settings due to leaching of highly soluble compounds was also observed. A further decline in performance was observed in mixes containing recycled aggregates. Alkali activated municipal solid waste incinerator bottom ash presented fast carbonation but also a considerable strength enhancement. Highlights: Municipal solid waste bottom ash as precursor in alkali activated mortars. Production of hydrogen gas led to increased porosity and performance loss. Setting was not observed in mixes cured in ambient temperature. Formation of stable compounds after carbonation leading to strength increase.