Early hydration of belite-ye'elimite-ferrite cements: Role of admixtures. (31st March 2023)

• Record Type: Journal Article
• Authors: Pérez-Bravo, Raquel; Morales-Cantero, Alejandro; Cuesta, Ana; Aranda, Miguel A.G.; Santacruz, Isabel; De la Torre, Angeles G.
• Is Part Of: Construction & building materials. Volume 371(2023)
• Publication Date: 2023-03-31
• Subjects: CO2 footprint -- CaCl2 -- TIPA -- Rietveld analysis -- Synchrotron radiation; Building materials -- Periodicals; 624.18
• DOI: 10.1016/j.conbuildmat.2023.130765
• Languages: English
• ISSNs: 0950-0618

Abstract

Highlights: TIPA has promoted the precipitation of more AFt in the first 24 h of BYF hydration when compared to the reference paste without any admixture. CaCl2 has promoted the formation of higher amounts of amorphous calcium aluminum hydrates in the first 24 h. Neither TIPA nor CaCl2 has promoted the hydration of α ' H -belite in the first 24 h of hydration. The addition of TIPA or CaCl2 has enhanced the mechanical strengths of BYF mortars when compared to the reference mortar without any admixture. Abstract: The effect of TIPA and CaCl2 on early hydration, i.e. 24 h, of a B-BYF cement has been studied by in situ synchrotron X-ray powder diffraction, calorimetry, thermal analysis, NMR, and rheological measurements of the pastes and mechanical strength of the corresponding mortars. The addition of 0.05 % bwc (by weight of cement ) of TIPA reduced the viscosity of the paste during the first minutes of hydration but, after the end of the induction period, ∼7 h, it favored the formation of AFt compared to the reference paste. The latter is likely due to the acceleration of the dissolution of the amorphous aluminates and sulfates by the presence of TIPA. These results correlate with the increase of ∼169% of the 1-day mechanical strengths. The addition of 2.0 % bwc of CaCl2 accelerated the dissolution rate of ye'elimite, causing an increase of the amount of precipitated ettringite even before the end of the induction period, which has been shorted to ∼6 h. The 1-day mechanical strengths of the mortars with this admixture outperforms that of the reference mortar by 181%. Finally, ferrite and α ' H -belite reactivities were not affected by the addition of any of these admixtures during the first 24 h of hydration of this cement.