Novel method on homogenized La treatment of GCr15 steel by the self-reaction of La2O3 containing slag and steel for vacuum electroslag remelting. (May 2023)

• Record Type: Journal Article
• Authors: Li, Tengfei; Li, Guangqiang; Wang, Xijie; Deng, Xiaoxuan; Liu, Yu
• Is Part Of: Vacuum. Volume 211(2023)
• Publication Date: 2023-05
• Subjects: GCr15 steel -- La treatment -- Inclusions -- Vacuum electroslag remelting -- La2O3 slag; Vacuum -- Periodicals; 621.55
• DOI: 10.1016/j.vacuum.2023.111966
• Languages: English
• ISSNs: 0042-207X

Abstract

Abstract: The interaction between slag and GCr15 steel under argon and vacuum were investigated by laboratory experiments. The results show that the maximum and average size of inclusions, and the proportion of large inclusions decrease after slag-steel interaction. Compared with the test under argon, inclusion size of the steel in the test under vacuum is smaller and more uniform, which is attributed to that vacuum promotes the reaction of C and O in molten steel to form CO. The La content increase from 0 to 0.0022 wt% in the steel processed by La2 O3 containing slag after for 5 min holding at 1873 K under 0.5 kPa. Thermodynamic calculation reveals that the La2 O3 in molten slag can be reduced by dissolved C in liquid steel to form dissolved La under vacuum due to the relatively higher carbon content of GCr15 steel and appropriate vacuum condition. The microstructure and primary carbides of the tested steel under vacuum are finer than that under argon. The present study provides a theoretical basis for the homogenized La treatment of GCr15 steel under vacuum, which shows a promising prospect in vacuum electroslag remelting of high-end bearing steel. Highlights: Proposed a novel method for on homogenized La treatment of GCr15 steel. The La treatment by interaction between La2 O3 containing slag and dissolved C in steel under vacuum is feasible. The distribution of dissolved La in liquid steel by this method would be even due to the even distribution of reactans.