Hydrogen-assisted failure in Ni-based superalloy 718 studied under in situ hydrogen charging: The role of localized deformation in crack propagation. (15th April 2017)

• Record Type: Journal Article
• Authors: Tarzimoghadam, Z.; Ponge, D.; Klöwer, J.; Raabe, D.
• Is Part Of: Acta materialia. Volume 128(2017)
• Page Start: 365
• Page End: 374
• Publication Date: 2017-04-15
• Subjects: Alloy 718 -- Hydrogen embrittlement -- Planar slip -- Slip localization -- Hydrogen-enhanced localized plasticity; Materials -- Periodicals; Materials science -- Periodicals; Materials -- Mechanical properties -- Periodicals; Metallurgy -- Periodicals; Chemistry, Inorganic -- Periodicals; 620.112
• DOI: 10.1016/j.actamat.2017.02.059
• Languages: English
• ISSNs: 1359-6454

Abstract

Abstract: We investigated hydrogen embrittlement in Ni-based superalloy 718 by tensile testing at slow strain rate (10 −4 s −1 ) under continuous electrochemical hydrogen charging. Hydrogen-assisted cracking mechanisms were studied via electron backscatter diffraction (EBSD) analysis and electron channeling contrast imaging (ECCI). In order to elucidate the effects of stress or strain in the cracking mechanisms, material conditions with different strength levels were investigated, including samples in solution annealed (as water quenched) and 780 °C age-hardened states. The microstructure observations in the vicinity of the cracks enabled us to establish correlations between the microstructure, crack initiation sites, and crack propagation pathways. Fracture in the hydrogen-charged samples was dominated by localized plastic deformation. Strain-controlled transgranular cracking was caused by shear localization due to hydrogen-enhanced localized plasticity (HELP) and void nucleation and coalescence along {111} slip planes in both, the solution annealed and age-hardened materials. Stress-assisted intergranular cracking in the presence of hydrogen was only observed in the high strength age-hardened material, due to slip localization at grain boundaries, grain boundary triple junction cracking, and δ/γ-matrix interface cracking. To investigate the effect of δ-phase in crack propagation along grain boundaries, the over-aged state (aged at 870 °C) with different precipitation conditions for the δ-phase was also investigated. Observations confirmed that presence of δ-phase promotes hydrogen-induced intergranular failure by initializing micro-cracks from δ/γ interfaces. Graphical abstract: Image