Electrostatic crosslinking-enabled highly asymmetric lamellar nanostructures of polyzwitterionic block copolymers for lithography. Issue 9 (9th February 2023)

• Record Type: Journal Article
• Authors: Ding, Shi-Peng; Zhang, Ze-Kun; Ye, Ze; Xia, Ding-Li; Xu, Jun-Ting
• Is Part Of: Nanoscale. Volume 15:Issue 9(2023)
• Page Start: 4553
• Page End: 4560
• Publication Date: 2023-02-09
• Subjects: Nanoscience -- Periodicals; Nanotechnology -- Periodicals; 620.505
• DOI: 10.1039/d3nr00073g
• Languages: English
• ISSNs: 2040-3364

Abstract

Abstract : Intermolecular coulombic interactions induce physical crosslinking and thus the formation of highly asymmetric lamellar nanostructures in a broad composition range for polyzwitterionic block copolymers. Abstract : For the bulk self-assembly of traditional diblock copolymers (di-BCPs), lamellar structures only occur when two constituents have similar volume fractions ( f ) and two alternating layers tend to have similar thicknesses. Highly asymmetric lamellar (A-LAM) structures, in which the thickness of one layer is several times higher than the other, are hardly formed in di-BCPs, while they have potential applications in nanolithography. In this work, A-LAM structures with different dimensions were constructed using a type of simple linear di-BCP, polystyrene- b -poly(4-vinylpyridine)propane-1-sulfonate (PS- b -PVPS) with the polyzwitterionic block PVPS in minority. The origin of the A-LAM structure was ascribed to the electrostatic crosslinking and confirmed by doping PS- b -PVPS block copolymers (BCPs) with N -butyl pyridinium methane sulfonate (BPMS). The morphology of compositionally asymmetric PS- b -PVPS BCPs changed from A-LAM to cylindrical structures upon salt-doping, i.e. the phase behavior of common BCPs was recovered. In addition, the morphologies of PS- b -PVPS BCPs with similar molecular weights but varied compositions were also studied, and only two kinds of structures (lamellar or ill-defined spherical structure) were observed when the volume fraction of PVPS ( f PVPS ) was less than 0.5, and the composition range for the formation of the lamellar structure was found to be f PVPS ≥ 0.188.