Microstructure evolution during directional solidification of off-eutectic Al-Cu-Mg alloys. Issue 1 (1st January 2023)

• Record Type: Journal Article
• Authors: Ezemenaka, Dominic; Small, Samuel; Genau, Amber
• Is Part Of: IOP conference series. Volume 1274:Issue 1(2022)
• Publication Date: 2023-01-01
• Subjects: Materials science -- Periodicals; 620.1105
• DOI: 10.1088/1757-899X/1274/1/012035
• Languages: English
• ISSNs: 1757-8981

Abstract

Abstract: Building on previous studies of invariant ternary eutectic Al-Al2 Cu-Al2 CuMg, this work aims to deepen our understanding of the microstructural possibilities in the Al-rich region of the Al-Cu-Mg phase diagram by considering the solidification behaviour of several off-eutectic compositions. Four Al-Cu-Mg alloys were directionally solidified at a constant growth rate (1.25 μm/s) and thermal gradient (9-14 K/mm) using a Bridgman-type furnace and analysed using a combination of scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, and differential scanning calorimetry. Qualitative and quantitative analyses showed a preference for faceted Al2 Cu dendrites surrounded by a ternary eutectic matrix in the two Mg-poor samples, even though one composition was not in the primary Al2 Cu phase region. The two Al-poor samples consisted of large regions of three different intermetallic phases and little eutectic, making these samples very brittle.