Dynamic crack growth characteristics of half-circular disk PMMA specimens with prefabricated penetration defects under impact loading. (November 2020)

• Record Type: Journal Article
• Authors: Wang, Yanbing; Yu, Bingbing; Wu, Houwei; Lu, Keqin; Wang, Dongchen
• Is Part Of: Polymer testing. Volume 91(2020)
• Publication Date: 2020-11
• Subjects: Defects -- Caustics -- Crack growth -- Dynamic fracture; Polymers -- Testing -- Periodicals; Polymères -- Tests -- Périodiques; 620.1920287
• DOI: 10.1016/j.polymertesting.2020.106684
• Languages: English
• ISSNs: 0142-9418

Abstract

Abstract: In this paper, the dynamic fracture experiment of half-circular disk PMMA specimens with prefabricated penetration defects under impact loading was carried out on the digital laser dynamic caustics experimental system (DLDC), the law of crack initiation, growth and traversing under different tilt angles (30°, 45°, 60°) was examined, and the variations of crack growth trajectory, velocity and DSIF at crack tip were compared for analysis. In addition, the discrete lattice spring method (DLSM) as a new development was employed to simulate how the dynamic cracks grew in PMMA specimens with defects, it was found that the numerical model can reproduce the experiment phenomenon. On the basis, the effect of the elastic modulus of the penetration defect medium on crack growth was analyzed. Referring to the experiment and numerical results, it was thus concluded that the angle and the elastic modulus of penetration defect would dramatically influence the crack growth characteristics. Highlights: Combine the DLDC and DLSM together. Some value data were got. Some dynamic parameter were analyzed.