Influence of curing modes on conversion and shrinkage of dual-cure resin-cements. Issue 1 (January 2022)

• Record Type: Journal Article
• Authors: Aldhafyan, Mohammed; Silikas, Nikolaos; Watts, David C.
• Is Part Of: Dental materials. Volume 38:Issue 1(2022)
• Page Start: 194
• Page End: 203
• Publication Date: 2022-01
• Subjects: Dual-cure resin-cements -- Curing modes -- FTIR -- Degree of conversion -- Shrinkage; Dentistry -- Periodicals; Dental materials -- Periodicals; 617.695
• DOI: 10.1016/j.dental.2021.12.004
• Languages: English
• ISSNs: 0109-5641

Abstract

Abstract: Objective: To explore the effect of curing modes of dual-cure resin cements on their degree of conversion (DC) and polymerization shrinkage (PS) over specific post-activation periods. Methods: Five self-adhesive (PANAVIA SA, RelyX Universal Resin, RelyX Unicem 2, Bifix SE, and SpeedCEM Plus) and three conventional (PANAVIA V5, Nexus Third Generation, and RelyX Ultimate Universal) dual-cure resin cements were studied. Four specimens (n = 4) were made per curing mode (light/self-cure) to measure either DC or PS. FTIR was utilized to measure real-time DC (%) over 24 h. The Bonded Disk method was used to measure shrinkage at 23 °C over 1 h. The data were analyzed using one-way ANOVA, Tukey post-hoc tests and independent/ paired sample t -tests (a = 0.05). Results: After 1 h post-activation, the DC of light-cured (LC) specimens ranged between 66.6% and 77.4%, whereas for self-cured (SC) specimens DC ranged between 44.4% and 73.2%. After 24 h, the DC of LC specimens ranged between 74.8% and 82.4% and between 62.7% and 81.7% for SC specimens. After 24 h, the DC of three cements (BSE, PV5, and RXU) were comparable between their curing modes (p > 0.05), whereas five cements (CEM, NX3, PSA, RXU2, RXL) had significantly lower DC for SC compared to LC specimens (p < 0.05). After 1 h post-activation, shrinkage ranged between 5.9% and 8.5% for LC and between 4.9% and 8.3% for SC specimens. Most cements were not significantly different between curing modes. However, light-cured PAS, RXL and RXU2 had significantly higher shrinkage (p < 0.05). After 1 h post-activation, a strong positive correlation existed between conversion and shrinkage (LC: r 2 = 0.95 and SC: r 2 = 0.93). Significance: Whenever light access is possible, light-curing of resin-cements remains beneficial to the overall efficacy of their conversion and thus all factors that depend on that. Conversion and shrinkage behavior are intrinsically important factors in clinical selection of resin-cement products.