An investigation on the mechanisms of ant nest corrosion of copper tube in formic acid environment. Issue 1 (30th August 2022)

• Record Type: Journal Article
• Authors: Li, Haihong; Liu, Xiao; Li, Deshan; Wang, Zhongqi; Zhang, Xintao; Wang, Songwei
• Is Part Of: Materials and corrosion. Volume 74:Issue 1(2023)
• Page Start: 138
• Page End: 144
• Publication Date: 2022-08-30
• Subjects: ant nest corrosion -- copper tube -- formic acid -- mechanisms -- oxide layer; Materials -- Periodicals; Metals -- Periodicals; Corrosion and anti-corrosives -- Periodicals; 620.1122305
• DOI: 10.1002/maco.202213397
• Languages: English
• ISSNs: 0947-5117

Abstract

Abstract: Copper tubes used in air‐conditioners and refrigerators often fail due to ant nest corrosion (ANC) in formic acid environment. In this paper, corrosion behavior and corrosion mechanisms of copper tubes in formic acid (HCOOH) were analyzed by vapor corrosion tests, optical microscopy (OM), scanning electron microscope (SEM), energy‐dispersive X‐ray spectrometry (EDS). The effects of the surface condition on ANC of copper tube were also investigated. Results showed that ANC of copper tube was a spontaneous process. The surface integrity of copper tube surface oxide layer is not the decisive factor of ANC. ANC originated from the dissolution of the surface oxide layer in HCOOH, which exposed fresh copper matrix. ANC is a special electrochemical corrosion, where the copper matrix acts as an anode and the undissolved surface oxide layer acts as a cathode due to the potential difference. The accumulation of corrosion products consisting of Cu(HCOO)2 and Cu2 O can produce a wedge effect and generate many microcracks until to penetrate the copper tube wall. These findings would provide a deep understanding of the corrosion behavior of copper and copper alloys. Abstract : This study investigates the ant nest corrosion (ANC) behavior and corrosion mechanisms of copper tubes in formic acid. Results showed that ANC originated from the dissolution of the surface oxide layer in HCOOH and ANC is a special electrochemical corrosion. The accumulation of corrosion products can produce a wedge effect and generate many microcracks until to penetrate the copper tube wall.