Tensile properties of Z-pinned composite laminates with low damage insertion technique. Issue 1 (January 2021)

• Record Type: Journal Article
• Authors: Ma, C Y; Li, Y L; Chen, W; Li, X Q; Teng, X B; Xu, Y J; Liu, W W
• Is Part Of: Journal of physics. Volume 1765:Issue 1(2021)
• Publication Date: 2021-01
• Subjects: Physics -- Congresses; 530.5
• DOI: 10.1088/1742-6596/1765/1/012009
• Languages: English
• ISSNs: 1742-6588

Abstract

Abstract: In this paper, the effects of Z-pin diameter and Z-pin length on the tensile properties of carbon fiber reinforced laminates were studied. A new Z-pin insertion technique which causes less microdamage damage than the original method was developed. Experimental testing reveals that the in-plane tensile strength of Z-pin specimens is 96.98%-105.32% of the control group. The best performance of in-plane tensile properties is TF18 group which pinned by full-depth Φ0.18mm diameter. The tensile strength increases by 5.32%, and the Young's modulus increases by 4.71% relative to the control group. Compared with the group of large diameter Z-pin, the in-plane performance of the ultra-fine diameter group is better due to the less in-plane damage. In the half-depth group, delamination occurred between the middle Z-pin sublayer and the upper and lower layers, thus reducing the in-plane tensile property. The Poisson's ratio increases in both full depth and half depth after Z-pinned and it is only related to insertion depth.