Mechanical and thermal properties of PEEK composites by incorporating inorganic particles modified phosphates. (1st May 2021)

• Record Type: Journal Article
• Authors: Niu, Yongan; Zheng, Shuojin; Song, Pingan; Zhang, Xin; Wang, Chao
• Is Part Of: Composites. Number 212(2021)
• Publication Date: 2021-05-01
• Subjects: Phosphates -- Composites -- PEEK -- Compressive strength -- Thermal properties; Composite materials -- Periodicals; Materials science -- Periodicals; Composite materials; Periodicals; Electronic journals; 620.118
• DOI: 10.1016/j.compositesb.2021.108715
• Languages: English
• ISSNs: 1359-8368

Abstract

Abstract: This work aims to improve heat resistance and mechanical properties of PEEK composites by filling the modified phosphates with inorganic particles (Si3 N4, AlN, Al2 O3 and Cu2 O) as reinforcements. The modified phosphate/PEEK composites were successfully prepared by pre-mixing and compression molding. The crystalline structures and compositions of modified phosphates and composites are characterized. Furthermore, the thermal and mechanical properties of composites were evaluated by thermal aging resistance at 350 °C for 24 h. The results show that all the four kinds of phosphate reinforcements can enhance the thermal aging resistance of phosphate/PEEK composites to varied extent. For the modified phosphate by Al2 O3, its addition increases the 30% weight loss temperature ( T 30 ) by 55 °C. Moreover, the compressive strength exhibits a 105.6% enhancement, reaching 321.4 MPa from 156.3 MPa of the PEEK matrix. This work provides a valuable route to improve the thermal and mechanical properties of PEEK composites, which would have promise applications in heat-resistant and high-strength structural materials. Graphical abstract: Image 1 Highlights: Phosphates modified by Si3 N4, AlN, Al2 O3 and Cu2 O particles were used as the reinforcement of PEEK composites. Modified phosphate/PEEK composites could be prepared by molding and thermal treating at 350 °C. Modified phosphates have a sufficient impact of the thermal and mechanical properties of PEEK composites. T30 could be increased by about 55 °C, and the compressive strength was increased by 105.6%.