Characterization and evaluating the mechanical performance of halloysite nanotubes reinforced acrylonitrile butadiene styrene/polycarbonate composites exposed to aggressive environmental conditions. Issue 1 (23rd January 2023)

• Record Type: Journal Article
• Authors: Narendra Babu, Y.; Venkateswara Rao, M.; Gopala Krishna, A.
• Is Part Of: Materialwissenschaft und Werkstofftechnik. Volume 54:Issue 1(2023)
• Page Start: 81
• Page End: 89
• Publication Date: 2023-01-23
• Subjects: acidic environment -- composites -- halloysite nanotubes -- mechanical performance -- nanocomposites; Halloysit-Nanoröhrchen -- mechanische Eigenschaften -- Nanoverbundwerkstoffe -- säurehaltige Umgebung -- Verbundwerkstoffe; Materials -- Periodicals; Materials -- Testing -- Periodicals; 620.1
• DOI: 10.1002/mawe.202200140
• Languages: English
• ISSNs: 0933-5137

Abstract

Abstract: Developing light weight polymer based composites dispersed with novel reinforcements which can function well in the presence of aggressive environments is an active research field in the materials engineering. Hence, in the current work, halloysite nanotubes (1 %, 2 %, 4 %, 6 %, 8 % and 10 % by weight) were reinforced into acrylonitrile butadiene styrene/polycarbonate blend and the role of reinforcing phases on the mechanical performance under aggressive environmental conditions has been evaluated. Hardness was measured as gradually increased in the composites with the increased content of the reinforcements. Impact strength of the composites was observed as increased in the composites up to 4 % reinforcement and further decreased. Increased strength was measured for the composite up to 2 % reinforcement. Ductility of the composites was decreased as reflected form the decreased % of elongation with the higher fraction of reinforcements due to induced brittleness. The composites were exposed to diluted sulfuric acid for 3 h and 6 h at 60 °C and then subjected to tensile loading. With the increased time of exposure, composites with 1 % and 2 % reinforcement exhibited relatively better performance. Abstract : Composites of acrylonitrile butadiene styrene/polycarbonate ‐ halloysite nanotubes were prepared with different fractions of reinforcement. Composites exhibited increased hardness, impact strength and tensile properties. Composites with 1 % and 2 % halloysite nanotubes exhibited better strength and retained ductility when exposed to acidic environment at 60 °C.