Effect of heterojunction structures on photoelectrochemical properties of ZnTe-based photocathodes for water reduction. Issue 1 (22nd December 2022)

• Record Type: Journal Article
• Authors: Tanaka, Tooru; Tsutsumi, Ryusuke; Yoshinaga, Tomohiro; Sonoyama, Takaki; Saito, Katsuhiko; Guo, Qixin; Ikeda, Shigeru
• Is Part Of: RSC advances. Volume 13:Issue 1(2023)
• Page Start: 575
• Page End: 580
• Publication Date: 2022-12-22
• Subjects: Chemistry -- Periodicals; 540.5
• DOI: 10.1039/d2ra06301h
• Languages: English
• ISSNs: 2046-2069

Abstract

Abstract : ZnTe-based photocathodes with a n-ZnS/ZnTe/p-ZnTe structure showed superior H2 liberation rate, indicating the possibility to use this structure for artificial solar water splitting. Abstract : Photoelectrochemical (PEC) properties of ZnTe-based photocathodes with various structures were investigated to clarify the effective structure for the water reduction reaction. Samples with n-ZnO/ZnTe/p-ZnTe and n-ZnS/ZnTe/p-ZnTe heterostructures showed superior PCE properties to the samples without a heterojunction. In particular, the n-ZnS/ZnTe/p-ZnTe sample exhibited a large photocurrent even at a low applied potential in an electrolyte containing Eu 3+ ion as an electron scavenger. Appreciable H2 evolution with a constant rate (approximately 87 μmol cm −2 h −1 ) was also observed over the sample loaded with Pt deposits under visible-light irradiation (>420 nm): faradaic efficiency of almost 100% was obtained, indicating no unfavorable side reaction occurred in the sample.