Influence of weave architecture on mechanical response of SiCf-SiCm tubular composites. (December 2022)

• Record Type: Journal Article
• Authors: Nance, James; Subhash, Ghatu; Sankar, Bhavani; Kim, Nam-Ho; Deck, Christian; Oswald, Sarah
• Is Part Of: Materials today communications. Volume 33(2022)
• Publication Date: 2022-12
• Subjects: SiCf-SiCm composites -- Failure modes -- Tensile hoop test -- Rotating flexural test; Materials science -- Periodicals; 620.11
• DOI: 10.1016/j.mtcomm.2022.104206
• Languages: English
• ISSNs: 2352-4928

Abstract

Abstract: Due to their high resistance to radiation damage and elevated temperature, silicon carbide fiber-reinforced, silicon carbide matrix composites (SiCf -SiCm ) are identified as potential cladding structures for use in nuclear reactors. In this study, four composite architectures with varying ply numbers along the thickness direction and different biaxial or triaxial plain weave orientations at either 45° or 60°, were systematically evaluated under various stress states to assess the influence of weave architecture on mechanical performance. Experiments were conducted on SiCf -SiCm composite tubes under tensile hoop, axial compression, and rotating flexural loading to evaluate the mechanical response and investigate the failure modes using high-speed imaging and digital image correlation (DIC) techniques. It was found that for tensile hoop burst and flexural loading, the braiding angle had the most significant influence on the strength of the composite, whereas the effect of fiber angle was more limited for compression testing. Under axial compression a unique failure mode where a microcrack nucleates and grows only to a length equal to the thickness of a single yarn was identified. This crack growth behavior is reflected as periodic oscillations in the load-displacement response. For both axial and hoop loading, regardless of weave angle and number of plies, failure always initiated parallel to the tube axis in a single yarn and the cumulative interaction of these microcracks lead to either axial burst or fracture at an angle to the tube axis along a yarn. These results point to the importance of customizing the design of tube architecture for enhanced performance in specified nuclear applications. Graphical Abstract: ga1