Charge transfer mechanisms in 40SiO2-40P2O5-20ZrO2 /sulfonated styrene-ethylene-butylene-styrene hybrid membranes for low temperature fuel cells. (2nd December 2022) - Pascual-Jose, B.
Abstract: A series of hybrid membranes synthetized via sol-gel chemistry and direct infiltration method have been prepared, consisting of sulfonated styrene-ethylene-butylene-styrene block copolymer (sSEBS), as polymeric matrix, and a zirconia modified phosphosilicate (40SiO2 –40P2 O5 –20ZrO2 ) as inorganic component. The infiltration procedure has been carried out by immersion of sSEBS membranes in a 40SiO2 –40P2 O5 –20ZrO2 sol solution for 5, 10, 20, and 40 min. The hybrid infiltrated membranes (sSEBS-Zr) have been thermally characterized to further investigate their suitability as electrolytes for low temperature fuel cells. TGA thermograms showed that sSEBS-Zr were more thermally stable than sSEBS. DSC thermograms showed that the addition of inorganic component decreases the Tg of the polystyrene block in hybrid membranes sSEBS-Zr. DETA showed significant differences in the charge transfer mechanisms between low and high temperature regions. The through-plane proton conductivity analysis showed that the sSEBS-Zr infiltrated 10 min had a better proton conductive capacity at 333K, thus showing that longer infiltration times might induce excessive M-O-M′ bonds, causing competition for the available proton sites. These results indicated that the proposed methodology shows good agreement with experimental performance data in hydrogen PEMFCs. Nonetheless, when DMFCs are considered, minimizing the permeability of methanol enhances more the performance than increasing the proton conductivity. Graphical abstract: Image 1 Highlights: Hybrid membranes sSEBS-Zr possess better thermal stability than sSEBS ones. The Zr-filler modifies the transfer mechanism of sSEBS membranes at low temperatures. At high temperatures, sSEBS-Zr and sSEBS have the same conductivity mechanism. sSEBS-Zr membranes with 10 min of infiltration maximizes proton conductivity. sSEBS-Zr membranes are good candidates to be used as polymer electrolytes.