Biodeterioration of Sustainable Hemp Shive Biocomposite Based on Gypsum and Phosphogypsum. Issue 15 (23rd November 2022)

• Record Type: Journal Article
• Authors: Bumanis, Girts; Irbe, Ilze; Sinka, Maris; Bajare, Diana
• Is Part Of: Journal of natural fibers. Volume 19:Issue 15(2022)
• Page Start: 10550
• Page End: 10563
• Publication Date: 2022-11-23
• Subjects: Hempcrete -- gypsum -- phosphogypsum -- biodeterioration -- thermal conductivity -- molds; 血红素混凝土 -- 石膏 -- 磷石膏 -- 生物退化 -- 导热系数 -- 铸模; Textile research -- Periodicals; Textile research; Periodicals; 677.005
• DOI: 10.1080/15440478.2021.1997871
• Languages: English
• ISSNs: 1544-0478

Abstract

ABSTRACT: The present research investigated bio-based construction material based on hemp shives and gypsum. Low-density material was developed with densities of 200, 300, and 400 kg/m 3 . Simple yet robust production technology was used. For the first time, a binder for biocomposites obtained from phosphogypsum was used and properties were compared to commercial gypsum. CO2 negative building material was developed with up to 92 kg CO2 ekv./m 3 entrapped. Both physical and mechanical properties were studied. Thermal conductivity was in the range from 0.058 to 0.101 W/(m·K) and compressive strength from 0.10 to 0.57 MPa. Biodeterioration test results showed that the pH of 5.60–6.55 for biocomposites promoted a rapid mold growth. Mold growth was slightly lower for composites with higher gypsum content, while phosphogypsum induced more rapid mold growth. Cladosporium, Rhizopus, Chaetomium, and other molds were observed on samples even at an early stage of testing giving a serious concern about only limited application in dry conditions for such gypsum-based biocomposite.