Metallurgical performance and structural characteristics of cokes of hypercoal prepared from the mixture of low-rank coal and biomass residue. (15th January 2023)

• Record Type: Journal Article
• Authors: Zhao, Jun; Liu, Hong; Zhang, Haochen; Song, Xiaolin; Zuo, Haibin; Wang, Guangwei; Xu, Zhigao; Wu, Ming; Zhang, Zhenyue; Chi, Ru'an
• Is Part Of: Fuel. Volume 332(2023)Part 1
• Publication Date: 2023-01-15
• Subjects: Hypercoal -- Low-rank coal -- Biomass residue -- Coking -- Coke structure -- Coke strength; Fuel -- Periodicals; Coal -- Periodicals; Coal; Fuel; Periodicals; 662.6
• DOI: 10.1016/j.fuel.2022.126069
• Languages: English
• ISSNs: 0016-2361

Abstract

Highlights: HPC has shown better caking and fluid properties, 95 % and 35.48 mm. The suitable addition ratio of HPC in blending coking is 15 wt%. The vitrinite content and mean vitrinite reflectance of HPC are 95% and 0.352, respectively. Cold strength of the coke decreases with HPC augmentation when its content is higher than 20 wt%. Abstract: This study aimed to effectively utilize low-rank coal and biomass residue in the coking process. Hypercoal was produced through co-thermal extraction, and its performance as a component in the coking process was investigated. The effects of the amount of hypercoal extracted from 80 wt% low-rank coal and 20 wt% biomass residue on the coke strength and structure were investigated. Raman spectroscopy, optical microscopy, and scanning electron microscopy were used to analyze the carbonaceous, optical, and pore structures of the hypercoal coke. The optimal ratio of the coal blend contained 15 wt% hypercoal, with compressive and drum strengths of 7.76 MPa and 86 %, respectively. The vitrinite content and average maximum vitrinite reflectance of the hypercoal were 95 % and 0.352, respectively. High vitrinite contents in hypercoal contribute to the formation of mosaics within the coke, which can improve its cold strength. Moreover, the evolution of the hypercoal coke structure at various addition ratios was explored.