Templated‐Assembly of CsPbBr3 Perovskite Nanocrystals into 2D Photonic Supercrystals with Amplified Spontaneous Emission. Issue 40 (13th August 2020)

• Record Type: Journal Article
• Authors: Vila‐Liarte, David; Feil, Maximilian W.; Manzi, Aurora; Garcia‐Pomar, Juan Luis; Huang, He; Döblinger, Markus; Liz‐Marzán, Luis M; Feldmann, Jochen; Polavarapu, Lakshminarayana; Mihi, Agustín
• Is Part Of: Angewandte Chemie international edition. Volume 59:Issue 40(2020)
• Page Start: 17750
• Page End: 17756
• Publication Date: 2020-08-13
• Subjects: 2D photonic crystals -- amplified spontaneous emission (ASE) -- PDMS template -- perovskite nanocrystals -- self-assembly; Chemistry -- Periodicals; 540
• DOI: 10.1002/anie.202006152
• Languages: English
• ISSNs: 1433-7851

Abstract

Abstract: Perovskite nanocrystals (NCs) have revolutionized optoelectronic devices because of their versatile optical properties. However, controlling and extending these functionalities often requires a light‐management strategy involving additional processing steps. Herein, we introduce a simple approach to shape perovskite nanocrystals (NC) into photonic architectures that provide light management by directly shaping the active material. Pre‐patterned polydimethylsiloxane (PDMS) templates are used for the template‐induced self‐assembly of 10 nm CsPbBr3 perovskite NC colloids into large area (1 cm 2 ) 2D photonic crystals with tunable lattice spacing, ranging from 400 nm up to several microns. The photonic crystal arrangement facilitates efficient light coupling to the nanocrystal layer, thereby increasing the electric field intensity within the perovskite film. As a result, CsPbBr3 2D photonic crystals show amplified spontaneous emission (ASE) under lower optical excitation fluences in the near‐IR, in contrast to equivalent flat NC films prepared using the same colloidal ink. This improvement is attributed to the enhanced multi‐photon absorption caused by light trapping in the photonic crystal. Abstract : Perovskite nanocrystals (NCs) are self‐assembled into 2D photonic supercrystals using pre‐patterned polydimethylsiloxane (PDMS) templates and their optical spectra are tunable by varying the lattice spacing. These photonic crystals show amplified spontaneous emission (ASE) under lower optical excitation fluences in the near‐IR region due to enhanced multi‐photon absorption caused by light trapping in the photonic crystal.