AlCoCrFeNi-NiTi high entropy alloy composites: Microstructure and wear performance. (August 2022)

• Record Type: Journal Article
• Authors: Ghanbariha, M.; Farvizi, M.; Ebadzadeh, T.; Samiyan, A. Alizadeh; Kim, H.S.
• Is Part Of: Materials today communications. Volume 32(2022)
• Publication Date: 2022-08
• Subjects: AlCoCrFeNi HEA -- NiTi -- Sintering behavior -- Tribology -- Nanoindentation; Materials science -- Periodicals; 620.11
• DOI: 10.1016/j.mtcomm.2022.103952
• Languages: English
• ISSNs: 2352-4928

Abstract

Abstract: In the current research, AlCoCrFeNi–x wt% NiTi (x = 0, 5, and 10) high entropy alloy (HEA) composites were prepared using a combination of mechanical alloying and spark plasma sintering methods. Microstructural studies showed that the introduction of 5 wt% NiTi slightly changed the BCC and FCC fractions of the HEA matrix. However, in the HEA-10NiTi sample, which exhibited increase in the interfacial regions and acceleration of interdiffusion between elements, the (Ni, Al)-rich BCC phase fraction was considerably reduced. According to nano-indentation tests, the NiTi and BCC phases possess higher hardness-to-elastic modulus values that confirm the positive effect of these two phases on tribological behavior. Among the prepared specimens, HEA-5NiTi had the lowest wear rate (0.71 ± 0.01 mm 3 /N· m). This is attributable to the higher BCC phase fraction and reinforcing effect of the NiTi particles. Graphical Abstract: ga1