Adhesive Bond Integrity of Experimental Zinc Oxide Nanoparticles Incorporated Dentin Adhesive: An SEM, EDX, μTBS, and Rheometric Analysis. (10th August 2022)

• Record Type: Journal Article
• Authors: Alfaawaz, Yasser F.; Alamri, Renad; Almohsen, Fatimah; Shabab, Sana; Alhamdan, Mai M.; Al Ahdal, Khold; Farooq, Imran; Vohra, Fahim; Abduljabbar, Tariq
• Other Names: Ardelean Lavinia C. Academic Editor.
• Is Part Of: Scanning. Volume 2022(2022)
• Publication Date: 2022-08-10
• Subjects: Scanning electron microscopy -- Periodicals; 502.825
• DOI: 10.1155/2022/3477886
• Languages: English
• ISSNs: 0161-0457

Abstract

Abstract : Objective . Our study is aimed at preparing an experimental adhesive (EA) and assessing the influence of adding 5-10 wt.% concentrations of zinc oxide (ZnO) nanoparticles on the adhesive's mechanical properties. Methods . Field emission scanning electron microscopy (FESEM) and energy dispersive X-ray (EDX) spectroscopy were employed to investigate the morphology and elemental distribution of the filler nanoparticles. To examine the adhesive properties, microtensile bond strength ( μ TBS) testing, an investigation of the rheological properties, degree of conversion (DC), and analysis of the interface between the adhesive and dentin were carried out. Results . The SEM micrographs of ZnO nanoparticles demonstrated spherical agglomerates. The EDX plotting confirmed the incidence of Zn and oxygen (O) in the ZnO nanoparticles. The highest μ TBS was observed for nonthermocycled (NTC) 5 wt.% ZnO group (32.11 ± 3.60 MPa), followed by the NTC-10 wt.% ZnO group (30.04 ± 3.24 MPa). Most of the failures observed were adhesive in nature. A gradual reduction in the viscosity was observed at higher angular frequencies, and the addition of 5 and 10 wt.% ZnO to the composition of the EA lowered its viscosity. The 5 wt.% ZnO group demonstrated suitable dentin interaction by showing the formation of resin tags, while for the 10 wt.% ZnO group, compromised resin tag formation was detected. DC was significantly higher in the 0% ZnO (EA) group. Conclusion . The reinforcement of the EA with 5 and 10 wt.% concentrations of ZnO nanoparticles produced an improvement in the adhesive's μ TBS. However, a reduced viscosity was observed for both nanoparticle-reinforced adhesives, and a negotiated dentin interaction was seen for 10 wt.% ZnO adhesive group. Further research exploring the influence of more filler concentrations on diverse adhesive properties is recommended.