Positive electrode–Li metal crosstalk behavior-induced morphology change of Li deposits. Issue 34 (15th August 2022)

• Record Type: Journal Article
• Authors: Kim, Hyun-seung; Jeong, Goojin; Leem, Han Jun; Lee, Min A; Lee, Je-Nam; Woo, Sang-Gil; Yu, Jisang
• Is Part Of: Journal of materials chemistry. Volume 10:Issue 34(2022)
• Page Start: 17659
• Page End: 17667
• Publication Date: 2022-08-15
• Subjects: Materials -- Research -- Periodicals; Chemistry, Analytic -- Periodicals; Environmental sciences -- Research -- Periodicals; 543.0284
• DOI: 10.1039/d2ta03666e
• Languages: English
• ISSNs: 2050-7488

Abstract

Abstract : The critical mechanism underlying the degradation of the Li metal electrode and the positive electrode caused by operating voltage-dependent LiFSI-DME electrolyte decomposition is revealed. Abstract : The anomalous crosstalk behavior in lithium metal batteries using DME-based electrolytes is investigated. The oxidative decomposition of the LiFSI-DME electrolyte forms a film on the positive electrode and soluble products simultaneously. The quantity of soluble decomposition products is directly proportional to the cycling voltage; a 4.2 V cycled NCM811 positive electrode exhibits severe degradation and significant product yield. The soluble degradation products readily diffuse to the Li metal and form a resistive film. The film generated on the Li metal increases the polarization of Li deposition. The altered Li cycling kinetics from the crosstalk affects the deposition morphology of Li, leading to the formation of porous and dendritic deposits with a 4.2 V cycled NCM811 electrode, compared to the dense morphology observed in cells comprising LFP and Li. This new finding of soluble oxidative decomposition product-induced failure highlights a route to overcome the challenge of developing stable lithium metal batteries.