Floating catalyst chemical vapor infiltration of nanofilamentous carbon reinforced carbon/carbon composites – Integrative improvement on the mechanical and thermal properties. Issue 11 (September 2018)

• Record Type: Journal Article
• Authors: Deng, Hailiang; Li, Kezhi; Zheng, Jinhuang; Cui, Hong; Li, Hejun; He, Yizhu; Song, Guangsheng
• Is Part Of: Journal of the European Ceramic Society. Volume 38:Issue 11(2018)
• Page Start: 3793
• Page End: 3803
• Publication Date: 2018-09
• Subjects: Carbon/carbon composites -- Floating catalyst -- Nanofilamentous carbon -- Mechanical strength -- Thermal properties; Ceramic materials -- Periodicals; Composite materials -- Periodicals; Matériaux céramiques -- Périodiques; Composites -- Périodiques; Ceramic materials; Composite materials; Periodicals; Electronic journals; 666.05
• DOI: 10.1016/j.jeurceramsoc.2018.04.054
• Languages: English
• ISSNs: 0955-2219

Abstract

Abstract: Nanofilamentous carbon (NFC) reinforced carbon/carbon composites were produced by floating catalyst chemical vapor infiltration with ferrocene content ranging 0–2.0 wt%. The NFCs and increased graphitization degree led to an improvement on the mechanical and thermal properties. An excellent combination of high strength and thermal conductivity (TC), and low coefficient of thermal expansion (CTE) was reached by adding 0.5–0.8 wt% catalyst. When the content exceeded 0.8wt%, the strength and TC were decreased by the limited NFC growth and matrix transited from rough laminar to isotropic pyrocarbon. After the treatment of 2500 °C, the strength and CTE decreased whereas the TC was increased. With the catalyst contents at 0.5–0.8 wt%, the flexural and shear strength retention ratios achieved a high value of 73.1–74.5 and 79.1–79.4%, respectively, and the in-plane and out-of-plane TCs exhibited maxima of 339.1 and 72.5 W/(m K). Relatively low CTE was obtained at 2.0 wt% catalyst owing to the increased amount of cracks and pores.