Oxidation and degradation of amorphous SiAlN coating via forming Si-Si bond. (1st May 2021)

• Record Type: Journal Article
• Authors: Gao, Zhaohe; Kulczyk-Malecka, Justyna; Zhang, Zhenbo; Liu, Han; Zhang, Xinxin; Chen, Ying; Hill, Patrick; Kelly, Peter; Xiao, Ping
• Is Part Of: Corrosion science. Volume 183(2021)
• Publication Date: 2021-05-01
• Subjects: FIB-XPS -- Si-Si bond -- SiAlN amorphous coating -- Outward diffusion -- Oxidation -- Degradation; Corrosion and anti-corrosives -- Periodicals; 620.11223
• DOI: 10.1016/j.corsci.2021.109318
• Languages: English
• ISSNs: 0010-938X

Abstract

Graphical abstract: Highlights: After 1 h exposure at 1000 °C, no detectable oxide scale formed on SiAlN/Mo (750 nm) coatings whereas SiAlN/Mo (300 nm) formed oxide scale. The downward diffusion of Si followed by relatively faster downward diffusion of N generated excessive Si and lean N, forming Si-Si bond and depletion of N below 30% in outermost surface of SiAlN, thereby resulting in oxidation of outermost surface. This study uncovered that oxidation mechanism of amorphous nitrides was determined by elemental composition instead of widely reported amorphous or crystalline status. Abstract: The oxidation and degradation of amorphous SiAlN coatings consisting of Si3 N4 and AlN phases, with 750 nm or 300 nm Mo interlayers on Zr alloy in steam environment at 1000 °C were investigated. After 1 h exposure, no detectable oxide scale formed on SiAlN/Mo (750 nm) coatings whereas SiAlN/Mo (300 nm) formed oxide scale. The downward diffusion of Si followed by relatively faster downward diffusion of N generated excessive Si and lean N, forming Si-Si bond in outermost surface of SiAlN, thereby resulting in oxidation. The degradation mechanism of amorphous nitrides was determined by elemental composition instead of reported amorphous or crystalline status.