An in-situ microscale investigation into the fracture of wood-adhesive interphase by nanoindentation. (5th September 2022)

• Record Type: Journal Article
• Authors: Cao, Yizhong; Xu, Chuhang; Zhang, Qijun; Jin, Chunde; Wang, Siqun; Wu, Qiang
• Is Part Of: Construction & building materials. Volume 346(2022)
• Publication Date: 2022-09-05
• Subjects: Wood-adhesive interphase -- Fracture -- Nanoindentation -- Engineered wood-based composites -- Finite element analysis; Building materials -- Periodicals; 624.18
• DOI: 10.1016/j.conbuildmat.2022.128393
• Languages: English
• ISSNs: 0950-0618

Abstract

Highlights: Micropillar compression accompanied by FEA simulation was applied to investigate the fracture of wood-adhesive interphase. Yield strength of microscale wood-adhesive interphase was contingent with the interpenetrating polymer networks (IPNs). A crack-dominated fracture mode was found when compressing the wood-adhesive interphase comprising cell wall and adhesive. Abstract: Green timber high-rises now taking off raises the desire to improve the mechanical performance and durability of engineered wood-based composites. It requires an in-depth understanding of the fracture mechanism of wood-adhesive interphase. Nanoindentation (NI) analyses in conjunction with finite element analysis (FEA) were conducted in this work to reveal the fracture behaviors and static mechanical properties of microscale wood-adhesive interphases composed of different cell wall layers and phenol–formaldehyde (PF) adhesive. Results revealed the evident cracks and bending in microscale wood-adhesive interphase, which originates from the stress concentration at the interfacial interlock of the cell walls and PF adhesive. Deformation of compound middle lamella (CML) located far from the bond line was prior to other microscale wood-adhesive interphases. Prolongation of cracks contributes to the fracture of wood substrates, and brittle fracture of adhesive leads to the deconstruction of wood-adhesive interphase. Results also demonstrated that compact interpenetrating polymer networks (IPNs) impart the corresponding wood-adhesive interphase with the favored yield strength (281 MPa) because of the improved stress transferring. Therefore, building compact IPNs is beneficial for fabricating a strengthened and toughened wood-adhesive interphase in engineered wood-based composites.