Effect of Boron Distribution on the Intergranular Corrosion Resistance of UNS S32506 Duplex Stainless Steels. Issue 13 (1st January 2019)

• Record Type: Journal Article
• Authors: Takei, Takayuki; Yabe, Murotsune; Ooi, Azusa; Tada, Eiji; Nishikata, Atsushi
• Is Part Of: Journal of the Electrochemical Society. Volume 166:Issue 13(2019)
• Page Start: C375
• Page End: C381
• Publication Date: 2019-01-01
• Subjects: Corrosion -- boron -- Duplex stainless steel -- Intergranular Corrosion; Electrochemistry -- Periodicals; 541.3705
• DOI: 10.1149/2.1101912jes
• Languages: English
• ISSNs: 0013-4651

Abstract

Abstract : The effect of boron distribution on the intergranular corrosion (IGC) resistance of UNS S32506 duplex stainless steel (DSSs) was investigated. IGC tests in boiling nitric acid were conducted with DSSs with boron contents ranging from 1 to 50 ppm. The corrosion rate increased with increasing boron addition. Further addition of boron did not affect the IGC resistance. Microstructural observations, corrosion depth measurements, and secondary-ion mass spectrometry analysis revealed that the diminished IGC resistance was attributable to corrosion resistance degradation of α/γ interfaces due to boron segregation at the interfaces.