Highly efficient Co/NC catalyst derived from ZIF-67 for hydrogen generation through ammonia decomposition. (26th March 2022) - Li, Guoru
Abstract: Small-size cobalt nanoparticles (NPs) distributed on nitrogen doped carbon support (Co/NC-X) were prepared by pyrolysis of ZIF-67 at various temperatures (X = 500, 600, 700 and 800 °C) in nitrogen atmosphere and utilized as catalysts for hydrogen production through ammonia decomposition. Characterizations of the catalysts including XRD, HRTEM, XPS, H2 -TPR, CO2 -TPD, etc., were conducted for structure analysis. The N–C plate obtained from pyrolysis was coated with Co NPs to hinder its aggregation, which made the Co NPs dispersed evenly and increased their dispersion. The calcination temperature and the strong base of the support can adjust the strength of Co–N bond. The activity of the Co/NC-X catalysts is attributed to the high content of Co 0 and the moderate Co–N bond strength. The ammonia decomposition activity of Co/NC-X catalysts in this paper is higher than many reported Co-based catalysts. Co/NC-600 catalyst demonstrates an ammonia conversion of 80% at 500 °C with a space velocity of 30, 000 ml gcat −1 h −1, corresponding to a hydrogen production rate of 26.8 mmol H2 gcat −1 min −1 . The work provides insight for the development of highly active cobalt-based catalysts for hydrogen production through ammonia decomposition. Graphical abstract: Image 1 Highlights: Small-size cobalt nanoparticles distributed on nitrogen doped carbon support. The moderate Co–N bond strength plays a key factor on catalytic activity. Co/NC-600 catalyst demonstrates an ammonia conversion of 80% at 500 °C. The activity of catalysts is higher than many reported Co-based catalysts.