Bis(4-methyl phenyl)iodonium as an alternative component to diphenyliodonium in camphorquinone-based ternary initiating systems. Issue 10 (October 2020)

• Record Type: Journal Article
• Authors: Verzola, Karina C.; Dressano, Diogo; Saraceni, Cintia Helena Coury; Gonçalves, Luciano Souza; Hadis, Mohammed; Watts, David C.; Palin, William M.; Lima, Adriano Fonseca
• Is Part Of: Dental materials. Volume 36:Issue 10(2020)
• Page Start: 1282
• Page End: 1288
• Publication Date: 2020-10
• Subjects: Polymerisation -- Resin composite -- Shrinkage -- Ternary photoinitiator -- Photo-cure; Dentistry -- Periodicals; Dental materials -- Periodicals; 617.695
• DOI: 10.1016/j.dental.2020.06.002
• Languages: English
• ISSNs: 0109-5641

Abstract

Highlights: BPI can be used in ternary activation systems substituting DPI salt. Use of iodonium salts increase the polymerization shrinkage of resins. Ternary systems containing BPI improve the flexural strength and modulus of resins. Abstract: Objective: To evaluate the influence of different co-initiators (diphenyliodonium hexafluorophosphate - DPI - and bis(4-methyl phenyl)iodonium hexafluorophosphate – BPI) on chemical and mechanical properties of resins. Methods: Nine experimental resins (50% Bis-GMA and 50% TEGDMA, w/w) with 60 wt% filler particles were formulated. The initiating system used was camphorquinone (CQ-1 mol%) and ethyl dimethylaminobenzoate (EDAB-2 mol%). Experimental groups were established according to DPI and BPI quantities (0.25, 0.5, 0.75, and 1 mol%). The control group was a resin containing only CQ-EDAB. Light transmission through the resin during polymerisation was analysed with a UV–vis spectrophotometer. Real-time polymerisation of the systems was evaluated using an FTIR spectrometer. Real-time polymerisation shrinkage strain was evaluated, and the flexural strength and modulus of materials were obtained by 3-point bending. Experimental groups were statistically analysed by Analysis of Variance and Tukey's test ( α = 0.05). Dunnett's test was applied to compare experimental groups with control. Results: Light transmission rapidly increased initially for resins containing DPI or BPI. After 30 s cure, the irradiance on the lower surface of resin specimens was similar for all groups. After 10 s of light irradiation, groups containing DPI and BPI had higher conversion than the control. However, conversion after 120 s post-irradiation was similar for all groups. The rate of polymerisation, shrinkage strain, and the maximum strain rate were higher for groups containing DPI/BPI. The use of iodonium salts increased the flexural strength and flexural moduli of resins. Significance: DPI and BPI increased resin reactivity similarly. Increased rate of polymerization influenced light transmission through the resin in the first seconds of polymerisation and increased resin shrinkage and rate of shrinkage, as well as flexural strength and moduli.