Enhanced Energy-Storage Properties of Ta Modified BNT − BT − NN Lead-Free Ceramics. Issue 1 (4th December 2020)

• Record Type: Journal Article
• Authors: Nilkhao, Supakit; Sumang, Rattiphorn; Charoonsuk, Thitirat; Prasertpalichat, Sasipohn
• Is Part Of: Integrated ferroelectrics. Volume 214:Issue 1(2021)
• Page Start: 79
• Page End: 89
• Publication Date: 2020-12-04
• Subjects: BNT-BT -- energy storage properties -- lead-free -- dielectric properties; Ferroelectric devices -- Periodicals; Integrated circuits -- Periodicals; 537.244805
• DOI: 10.1080/10584587.2020.1857180
• Languages: English
• ISSNs: 1058-4587

Abstract

Abstract: Lead-free 0.9(0.92Bi0.5 Na0.5 TiO3 –0.08BaTiO3 )–0.1(NaNb(1- x ) Ta x O3 ) ceramics (abbreviated as BNBT − NN1- x T x ), x = 0, 0.25, 0.50, 0.75 and 1.00, were prepared by conventional solid-state mixed oxide route. The effects of Ta substitution on the crystal structure, morphology, dielectric, ferroelectric as well as energy-storage properties were systematically investigated. X-ray diffraction revealed a single-phase perovskite structure for x ≤ 0.75 with coexisting rhombohedral and tetragonal phases. With increasing Ta substitution, a weakening of tetragonal distortion was observed. The SEM micrographs of all samples displayed dense microstructure with an average grain size of 0.70–0.99 µm. Good temperature stability of dielectric properties was maintained in the whole range of Ta substitution. The composition with x = 0.25 showed an optimum energy-storage density of 0.37 J/cm 3 and the energy-storage efficiency of 75.1% at 50 kV/cm, thus indicating the promising application of BNBT–NN1-x Tx ceramics as energy-storage capacitors.