Preparation of optimum degreasing–sintering process for metal–polymer blending low temperature 3D printing. Issue 3 (30th November 2018)

• Record Type: Journal Article
• Authors: Wang, Chuansheng; Cai, Ning; Zhang, Dewei; Zhang, Jinxiu; Chang, Tianhao; Li, Shaoming; Chao, Yuqi; Hu, Jiquan
• Is Part Of: Rapid prototyping journal. Volume 25:Issue 3(2019)
• Page Start: 515
• Page End: 529
• Publication Date: 2018-11-30
• Subjects: 3D printer based on powder particle -- Degreasing–sintering process -- Low temperature -- Polymer material -- Stainless steel powder; Engineering design -- Periodicals; 620.004205
• DOI: 10.1108/RPJ-03-2018-0071
• Languages: English
• ISSNs: 1355-2546

Abstract

Abstract : Purpose: This purpose of this study was to develop a 3D printer based on powder particle. The best degreasing and sintering process of a blank body was investigated to obtain a metal product with high precision and high surface finish. This process will greatly reduce the difficulty and cost of forming a complex metal product with high application value. Design/methodology/approach: Stainless steel powder and polymer materials were mixed using a rubber mixing machine. The powders were granulated to prepare a mixed material. A powder feed 3D printer was used at low temperature (about 200°C) to print and degrease the body. A series of sintering experiments were performed to study the different sintering temperatures, and the physical and mechanical properties of the sample sintered under various conditions were compared to determine the best degreasing and sintering process. Findings: The reaction at 1, 370°C was the optimal route for the metal billet degreasing. The resulting metal products had fine structure and stable performance compared with the products with traditional powder metallurgy composition. Originality/value: Most 3D printed metal powder materials rely on imports, which are expensive and increase the manufacturing cost. These drawbacks limit the application and development of metal 3D printing technology to a certain extent. The successful study of this molding method greatly reduces the difficulty and cost of forming complex metal products with high application value. This report will provide valuable guidance for sintering process and forming methods.