Effects of temperature and Ti addition on high-temperature oxidation behaviors of Co-Al-W based superalloys. Issue 5 (1st July 2020)

• Record Type: Journal Article
• Authors: Ma, Chunmei; Yang, Songting; Zhang, Yuheng; Wang, Kaikun; Fu, Huadong
• Is Part Of: Anti-corrosion methods and materials. Volume 67:Issue 5(2020)
• Page Start: 445
• Page End: 451
• Publication Date: 2020-07-01
• Subjects: High temperature -- Oxidation -- Cobalt-based superalloys; Corrosion and anti-corrosives -- Periodicals; 620.11223
• DOI: 10.1108/ACMM-04-2020-2298
• Languages: English
• ISSNs: 0003-5599

Abstract

Abstract : Purpose: Due to the special service environment of superalloys, this paper aims to obtain effects of temperature and Ti addition on high temperature oxidation behavior of Co-Al-W-B alloys. Design/methodology/approach: Isothermal oxidation experiment of Co-Al-W-based alloys were carried out at 800°C, 900°C and 1000°C for different times (3, 5, 10, 20, 50 and 100 h) referring to the method of HB5258-2000. Oxidation weight gain curves and oxidation products were detected. Findings: The results showed that the average oxidation rates of Co-Al-W-B alloy at 800 °C and 900 °C were 0.489 g·m −2 ·h −1 and 0.888 g·m −2 ·h −1, respectively, which belonged to an antioxidant grade. However, the average oxidation rate at 1000 °C was 2.068 g m −2 ·h −1, belonging to the secondary oxidation resistance class. In the alloy with Ti addition, dense Ti oxides film were formed at the early oxidation stage and then gradually diffused later, which can increase the oxidation resistance of the alloys to some extent. By analyzing the oxidation products of Co-Al-W-B alloy, it was found that a dense Al2 O3 layer could be formed when the alloy was oxidized at 800°C. The continuous Al2 O3 layer would prevent the oxygen from further spreading and make the alloy into the stable oxidation stage. However, only a non-dense Al2 O3 layer were observed with 900°C oxidation. Originality/value: It can provide references for the composition design, preparation process optimization and protective coating selection of the γ′ phase strengthened cobalt-base superalloys.