Effects of external hydrogen on hydrogen-assisted crack initiation in type 304 stainless steel. Issue 3 (30th April 2020)

• Record Type: Journal Article
• Authors: Chen, Xingyang; Ma, Linlin; Xie, Haoping; Zhao, Fengting; Ye, Yufeng; Zhang, Lin
• Is Part Of: Anti-corrosion methods and materials. Volume 67:Issue 3(2020)
• Page Start: 331
• Page End: 335
• Publication Date: 2020-04-30
• Subjects: Fatigue crack growth -- Stainless steel -- Crack initiation -- Hydrogen environment embrittlement; Corrosion and anti-corrosives -- Periodicals; 620.11223
• DOI: 10.1108/ACMM-02-2020-2258
• Languages: English
• ISSNs: 0003-5599

Abstract

Abstract : Purpose: The purpose of this paper is to present a crack initiation mechanism of the external hydrogen effect on type 304 stainless steel, as well as on fatigue crack propagation in the presence of hydrogen gas. Design/methodology/approach: The effects of external hydrogen on hydrogen-assisted crack initiation in type 304 stainless steel were discussed by performing fatigue crack growth rate and fatigue life tests in 5 MPa argon and hydrogen. Findings: Hydrogen can reduce the incubation period of fatigue crack initiation of smooth fatigue specimens and greatly promote the fatigue crack growth rate during the subsequent fatigue cycle. During the fatigue cycle, hydrogen invades into matrix through the intrusion and extrusion and segregates at the boundaries of α′ martensite and austenite. As the fatigue cycle increased, hydrogen-induced cracks would initiate along the slip bands. The crack initiation progress would greatly accelerate in the presence of hydrogen. Originality/value: To the best of the authors' knowledge, this paper is an original work carried out by the authors on the hydrogen environment embrittlement of type 304 stainless steel. The effects of external hydrogen and argon were compared to provide understanding on the hydrogen-assisted crack initiation behaviors during cycle loading.