Effects of pozzolanic reaction on carbonation degree and strength of steel slag compacts containing zeolite. (29th March 2021)

• Record Type: Journal Article
• Authors: Chang, Jun; Zhang, Xiong; Gu, Yang yang; Zhang, Yang yang
• Is Part Of: Construction & building materials. Volume 277(2021)
• Publication Date: 2021-03-29
• Subjects: Steel slag -- Zeolite -- Pozzolanic reaction -- Carbonation degree -- CaCO3 -- C-S-H gel; Building materials -- Periodicals; 624.18
• DOI: 10.1016/j.conbuildmat.2021.122334
• Languages: English
• ISSNs: 0950-0618

Abstract

Highlights: A novel method, zeolite partially replacing steel slag, was found to further improve the compressive strength and carbonation degree of steel slag compacts by accelerated carbonation curing. In terms of compressive strength and carbonation degree, the optimum content of steel slag substituted by zeolite was 5 wt.% and 15 wt.%, respectively. XRD, QXRD, TG, FT-IR, ICP-OES, MIP and SEM had been done to analyse the mechanism of zeolite improving carbonation degree and compressive strength of steel slag compacts. Abstract: In this paper, a novel method, zeolite partially replacing steel slag, was proposed to futher improve the properties (compressive strength and carbonation degree) of steel slag compacts futher after CO2 curing. Inductively coupled plasma (ICP) results illustrated that the Ca, and, Fe ion concentrations in the steel slag matrix substituted by 5 wt% zeolite (water-to-solid ratio of 10) were 78.19 mg/L and 4.09 mg/L, 19.3% and 99.0% higher than that of pure steel slag after 1 d of hydration curing respectively. The decreased crystallite size of C4 AF and increase in Fe ion concentration illustrates that zeolite with pozzolanic properties could react with CaO-FeO X matrix components such as brownmillerite (C4 AF), to produce C-S-H gel, which possesses higher solubility than the CaO-FeO X matrix, to improve the Ca ion concentration. In terms of the compressive strength and carbonation degree results, the optimum zeolite substitution ratios were 5 wt% and 15 wt%, respectively. After 1 d hydration and 2 h of carbonation curing, the compressive strength of the steel slag compacts with 5 wt% zeolite (CSZ5) was 14% higher than that of pure steel slag compacts (CSZ0). With respect to carbonation degree, the steel slag substituted with 15 wt% zeolite (CSZ15) had a 10.2% higher carbonation level than that of CSZ0.