Experimental Analysis of Short-Circuit Scenarios Applied to Silicon-Graphite/Nickel-Rich Lithium-Ion Batteries. Issue 2 (1st February 2022)

• Record Type: Journal Article
• Authors: Sturm, J.; Friedrich, S.; Genies, S.; Buzon, D.; G., Rahn-Koltermann; Rheinfeld, A.; A., Jossen
• Is Part Of: Journal of the Electrochemical Society. Volume 169:Issue 2(2022)
• Publication Date: 2022-02-01
• Subjects: lithium-ion battery -- short-circuit -- high-energy -- safety; Electrochemistry -- Periodicals; 541.3705
• DOI: 10.1149/1945-7111/ac51f3
• Languages: English
• ISSNs: 0013-4651

Abstract

Abstract : Short-circuit incidents pose a severe safety threat to lithium-ion batteries during lifetime. Understanding the underlying electrochemical behavior can help to mitigate safety risks. The electrochemically-caused rate-limiting behavior is analyzed using a quasi-isothermal test-bench, where external and local short-circuit conditions are applied to single-layered pouch cells (<50 mAh). The cell voltage, the heat generation rate, and either the short-circuit current or a local electrical potential are measured and used to characterize the short-circuit intensity. The results of 35 custom-built silicon-graphite SiC/NCA and SiC/NMC-811 cells with 2.5 wt.-% silicon are benchmarked to previously studied graphite G/NMC-111 cells. An additional current plateau appears for the silicon-graphite/nickel-rich cells, which is ascribed to the anode-limited electrode balancing. At a maximum, 29% of the total dissipated heat is caused during over-discharge. The effect of cyclic aging on the impact of the short-circuit behavior is investigated with aged single-layered pouch cells (SoH < 80%), which revealed nearly the same levels of over-discharge as non-aged cells. A lithium reference electrode is used to visualize polarization effects in the anode during ESCs and to evaluate the onset of copper dissolution (>3.2 V vs Li/Li + ), which could be estimated up to 20% of the negative current collector mass.