Damage and fracture analyses of wire with off-center inclusion on multi-pass drawing under different back tensions. (September 2022)

• Record Type: Journal Article
• Authors: Ma, Ao; Zhang, Yu; Dong, Liming; Yan, Hua; Fang, Feng; Li, Zhaoxia
• Is Part Of: Engineering failure analysis. Volume 139(2022)
• Publication Date: 2022-09
• Subjects: Multi-pass drawing -- Damage evolution -- Drawing fracture -- Back tensions -- Off-center inclusion; System failures (Engineering) -- Periodicals; Fracture mechanics -- Periodicals; Reliability (Engineering) -- Periodicals; Pannes -- Périodiques; Rupture, Mécanique de la -- Périodiques; Fiabilité -- Périodiques; Fracture mechanics; Reliability (Engineering); System failures (Engineering); Periodicals; Electronic journals; 620.112
• DOI: 10.1016/j.engfailanal.2022.106512
• Languages: English
• ISSNs: 1350-6307

Abstract

Highlights: Necking fracture of wire is caused by the extension of internal cracks to the surface. The damage and its growth rate will gradually increase as the back tension increases. The drawing fracture will be formed by greater damage if back tension is larger. The wire with inclusion will break earlier than that without inclusion during drawing. The existence of inclusion and back tension increase the risk of wire breakage. Abstract: The occurrence of fracture during wire drawing seriously reduced the quality of steel wire. In this study, the morphology of necking fracture and microstructure of wire are observed by SEM. It is found that there is large off-center inclusion on the surface of some fractures. Meanwhile, void defects appear near the inclusions, especially along the drawing direction. The FEM is employed to simulate multi-pass drawing of wire with and without off-center inclusion under different back tensions. The results show that with the increase of back tension, the damage in the core of wire without inclusion gradually accumulates. When the damage exceeds the critical value, cracks occur preferentially in the wire core and propagate to the surface of wire, thus forming as necking fracture. When the wire contains inclusion, cracks will first occur at both ends of inclusion, and its fracture is formed earlier than the wire without inclusion.