Compositional investigation of ∼2 μm luminescence of Ho3+-doped lead silicate glass. (November 2015)

• Record Type: Journal Article
• Authors: Liu, Xueqiang; Huang, Feifei; Gao, Song; Wang, Xin; Hu, Lili; Chen, Danping
• Is Part Of: Materials research bulletin. Volume 71(2016)
• Page Start: 11
• Page End: 15
• Publication Date: 2015-11
• Subjects: A. Glasses -- B. Optical properties -- C. Raman spectroscopy; Materials -- Periodicals; Crystal growth -- Periodicals; Matériaux -- Périodiques; Cristaux -- Croissance -- Périodiques; Crystal growth; Materials; Periodicals; 620.11
• DOI: 10.1016/j.materresbull.2015.06.049
• Languages: English
• ISSNs: 0025-5408

Abstract

Graphical abstract: Ho 3+ -doped lead silicate glass with lowest maximum phonon energy possesses highest ∼2 μm luminescence intensity. Highlights: With increment of lead oxide, maximum phonon energy in lead silicate glass decreased. ∼2 μm luminescent intensity of Ho 3+ increased with increment of lead oxide. Lowest lead oxide content glass possesses highest quantum efficiency due to low maximum phonon energy. Abstract: Lead silicate glass samples with varying lead oxide content were prepared in this study, and their luminescent properties were examined and analyzed. It was found that with increasing lead oxide content, the maximum phonon energies of the glass samples decreased, while their spontaneous transition probabilities first increased and then decreased. The influence of the spontaneous transition rate, A10, and the multi-phonon relaxation rate, W 10, on the sample luminescent properties was analyzed using rate equations. As a result, it was found that with increasing lead oxide content, W 10 / A 10 decreased, while the quantum efficiency increased. Thus, the luminescent intensity at ∼2 μm increased in the glass samples with increased lead oxide content. The high luminescent intensity and long lifetime indicate that silicate glasses containing high levels of lead oxide could potentially be used in ∼2 μm lasers.