Long-Term Effects of Humidity on Stainless Steel Pitting in Sea Salt Exposures. Issue 2 (1st February 2021)

• Record Type: Journal Article
• Authors: Srinivasan, J.; Weirich, T. D.; Marino, G. A.; Annerino, A. R.; Taylor, J. M.; Noell, P. J.; Griego, J. J. M.; Schaller, R. F.; Bryan, C. R.; Locke, J. S.; Schindelholz, E. J.
• Is Part Of: Journal of the Electrochemical Society. Volume 168:Issue 2(2021)
• Publication Date: 2021-02-01
• Subjects: Atmospheric corrosion -- stress corrosion cracking -- chloride; Electrochemistry -- Periodicals; 541.3705
• DOI: 10.1149/1945-7111/abdc75
• Languages: English
• ISSNs: 0013-4651

Abstract

Abstract : Ground 304 stainless steel (SS) samples were exposed to sea salt particles at 35 °C and two relative humidity (RH) levels for durations ranging from 1 week to 2 years. For all exposure times, pit number density and total pit volume at 40% RH were observed to be considerably greater than those at 76% RH. Statistical analysis of distributions of pit populations for both RH conditions showed that pit number density and total pit volume increased rapidly at first but slowed as exposure time increased. Cross-hatched features were observed in the 40% RH pits while ellipsoidal, faceted pits were observed at 76% RH. Optical profilometry indicated that most pits were not hemispherical. X-ray tomography provided evidence of undercutting and fissures. Piecewise curve fitting modeled the 40% RH data closely, predicting that corrosion damage would eventually plateau. However, a similar treatment of the 76% RH data suggested that corrosion damage would continuously increase, which implied that the piecewise power-law fit was limited in its ability to model atmospheric corrosion generally. Based on these observations, the operative mechanisms determining long-term corrosion behavior were hypothesized to be different depending on the RH of exposure.