Investigation of Poly(dimethylsilylene ethynylenealkylphenylenmethylenealkylphenyleneethynylene). Issue 11 (24th July 2022)

• Record Type: Journal Article
• Authors: Liu, Xiaotian; Ma, Manping; Li, Jixian; Gong, Changjun; Qiao, Zhiyao; Huang, Farong
• Is Part Of: Polymer-plastics technology and materials. Volume 61:Issue 11(2022)
• Page Start: 1153
• Page End: 1165
• Publication Date: 2022-07-24
• Subjects: Silicon-containing arylacetylene resin -- poly(dimethylsilylene-ethynylenealkylphenylenemethylenealkylphenyleneethynylene) -- high performance resin -- effect of side groups on an arylacetylene unit; Polymers -- Periodicals; Polymerization -- Periodicals; Plastics -- Periodicals; Plastics; Polymerization; Polymers; Periodicals; 668
• DOI: Https://www.tandfonline.com/doi/10.1080/25740881.2022.2039188
• Languages: English
• ISSNs: 2574-0881

Abstract

ABSTRACT: A new kind of silicon-containing arylacetylene resins with the structure unit of ethynylenealkylphenylenemethylenealkylphenyleneethynylene in the main chains were synthesized. Their structures were characterized by 1 H-NMR, FT-IR, Gel Permeation Chromatography (GPC), and X-Ray Diffraction (XRD). Properties of the resins such as solubility, softening point, viscosity, and processing window were determined. The mechanical properties and thermal stability of the cured resins and composites were tested. The results show that poly(dimethylsilylene ethynylenemethylphenylenemethylenemethylphenyleneethynylene) (PSMA-M) has good comprehensive performance. The flexural strength of the resin casting and its carbon fiber reinforced composite reaches 42.1 MPa and 381.9 MPa, respectively. The temperature (Td5 ) at 5% weight loss is 493°C under nitrogen. Graphical abstract: uf0001