Cation‐Structure Effects on Zinc Electrodeposition and Crystallographic Orientation in Ionic Liquids. Issue 10 (11th March 2022)

• Record Type: Journal Article
• Authors: Shimizu, Masahiro; Sugiyama, Yusuke; Horita, Masaomi; Yoshii, Kazuki; Arai, Susumu
• Is Part Of: ChemElectroChem. Volume 9:Issue 10(2022)
• Page Start: n/a
• Page End: n/a
• Publication Date: 2022-03-11
• Subjects: Electrodeposition -- Ionic Liquids -- Cation Structure -- Crystallographic Orientation -- Zn Deposition; Electrochemistry -- Periodicals; 541.37
• DOI: 10.1002/celc.202200016
• Languages: English
• ISSNs: 2196-0216

Abstract

Abstract: The electrochemical behavior of Zn deposition in room temperature ionic liquids consisting of bis(trifluoromethanesulfonyl)amide (TFSA − ) combined with N ‐propyl‐ N ‐methylpyrrolidinium (Pyr1, 3 + ) or 1‐ethyl‐3‐methylimidazolium (EMI + ) was investigated in terms of their physicochemical properties and dissolved Zn 2+ species. The effect of cation structure was examined not only on the macroscopic morphologies, but also on the microscopic aspects of crystallographic orientation of Zn deposits obtained from [Zn(TFSA)2 ]0.1 [ Cation ‐TFSA]0.9 . Electron backscattered diffraction revealed that the crystal grains grown in Pyr1, 3 ‐TFSA at the current density of 0.5 mA cm −2 were much finer, compared with the sizes of those in EMI‐TFSA. This is probably because Pyr1, 3 cations inhibit the surface diffusion of Zn adatoms, thus preventing growth in a specific plane direction. It was found that higher reversibility on Zn stripping needs larger crystal grains rather than polycrystalline with fine grains. The obtained results will contribute greatly to the realization of longer life batteries using Zn without resource constraints. Abstract : Zn electrodeposition : Electron backscattered diffraction revealed that the sizes of crystal grain and the crystal orientation as well as the morphology of Zn electrochemically grown at a galvanostatic condition varied depending on the cation structures of ionic liquids. It was found that higher reversibility on Zn stripping needs larger crystal grains rather than polycrystalline with fine grains.