Effect of TiO2 and 11 minor elements on the reactivity of ground‐granulated blast‐furnace slag in blended cements. Issue 1 (19th September 2020) - Blotevogel, Simon
Abstract: Ground‐granulated blast‐furnace slags (GGBS) are glasses (>99%) of the CaO‐Al2 O3 ‐SiO2 compositional system and are widely used as supplementary cementitious materials. Differences in reactivity of GGBS were screened by modifying the content of 12 minor elements (namely Ba, Ce, Cs, Cr, K, Mn, P, Sn, Sr, Ti, V, and Zr). Scanning electron microscopy observations showed that most elements entered the silicate glass matrix, only Sn was reduced to its metallic form and P accumulated in minor minerals. Mortar strength tests showed that 2 day compressive strength was reduced by >50% for a TiO2 content of 2.5 wt% in the slag. At 28 days the loss in compressive strength was still >40%. Calorimetric tests on other element additions showed that the content of network modifiers (Ba, Cs, K and Sr) and GGBS reactivity are positively correlated, whereas Ce, Cr, V, and Zr significantly decreased reactivity. Finally, it is shown that these effects can be estimated by the concentration and the weighted field strength of the added element.