Assessment of corrosion protection and performance of bio-based polyurethane acrylate incorporated with nano zinc oxide coating. (July 2020)

• Record Type: Journal Article
• Authors: Ariffin, Muhammad Mirza; Aung, Min Min; Abdullah, Luqman Chuah; Salleh, Mek Zah
• Is Part Of: Polymer testing. Volume 87(2020)
• Publication Date: 2020-07
• Subjects: Polyurethane acrylate -- Corrosion -- ZnO -- Hybrid coating -- EIS; Polymers -- Testing -- Periodicals; Polymères -- Tests -- Périodiques; 620.1920287
• DOI: 10.1016/j.polymertesting.2020.106526
• Languages: English
• ISSNs: 0142-9418

Abstract

Abstract: In this study, a series of UV-curable anticorrosive PUA coatings embedded with varying concentrations of inorganic ZnO fillers have been successfully prepared from jatropha-based polyol. The electrochemical impedance spectroscopy (EIS) and Tafel polarisation analysis revealed that increasing fillers composition lead to the improvement of the anticorrosive property of the hybrid coatings. Meanwhile, the salt spray test results were found to correlate with the EIS of Cc (F cm −2 ) was 2.71 × 10 −9, Bode plot - 10 6 Ω cm 2 and Tafel polarisation results 7.56 × 10 −6 MPY at 3 wt% of ZnO. Physical properties of 3 wt% loading of ZnO fillers in hardness test obtained 6H which was strongly attributed to the low interfacial interaction and poor dispersion of the fillers within the polymer matrix. Highlights: Bio-based PUA with ZnO coating showed significantly enhanced corrosion resistance. The incorporation of ZnO filler particle in organic coating matrix has good performance in coating. The morphology and XRD analysis was support for corrosion resistance and as well coating performance.