Investigation on graphene addition on the quasi-static and dynamic responses of carbon fibre-reinforced metal laminates. (May 2022)

• Record Type: Journal Article
• Authors: Wang, Shuo; Cao, Meng; Xue, Hongqian; Araby, Sherif; Abbassi, Fethi; He, Yanli; Su, Weiguo; Meng, Qingshi
• Is Part Of: Thin-walled structures. Volume 174(2022)
• Publication Date: 2022-05
• Subjects: FMLs -- Graphene nanoplatelets -- Charpy impact -- Three-point flexure -- Numerical simulation -- Damage analysis; Thin-walled structures -- Periodicals; 690.1
• DOI: 10.1016/j.tws.2022.109092
• Languages: English
• ISSNs: 0263-8231

Abstract

Abstract: In this paper, graphene nanoplatelets (GnPs) were used with carbon fibre/epoxy composite to enhance the mechanical performance of fibre metal laminates (FMLs). The designed FMLs are composed of thin aluminium alloy layers alternating with carbon-fibre epoxy/GnP composite plies with a chemical treatment performed on the aluminium laminate to promote adhesion strength with the epoxy composite. Two different configurations of FMLs were investigated (i) composite plies with unidirectional carbon fibres (U-FMLs) and (ii) composite plies with plain carbon woven (W-FMLs). Samples were tested under dynamic loading (Charpy impact) and quasi-static loading (three-point flexure). The experimental results showed that FMLs with 0.3 wt% GnPs logged the best impact performance; the impact strength of W-FMLs and U-FMLs are respectively 18.2% and 25.2% higher than FMLs without GnPs. FMLs with 0.5 wt% GnPs recorded the highest enhancement in flexural strength, fracture strain and flexural modulus recording increments 23.1%, 19.3% and 48% for the W-FMLs, and 60.3%, 34.5% and 61.4% for the U-FMLs, respectively. Also, an in-depth microscopic analysis was conducted to understand the reinforcing mechanism of GnPs into FMLs. Moreover, a numerical model of a three-point flexural test was developed to show the ability of numerical tools to predict material behaviour at optimized costs. Johnson–Cook and Hashin damage models were used respectively for aluminium alloy and carbon fibre epoxy/GnP composite to accurately predict their deformation and damage modes. Highlights: Investigate the effect of GnPs on the mechanical properties of FMLs with unidirectional and woven fibre layouts. Evaluate the influence of GnPs on the FMLs with unidirectional and woven fibres under dynamic and static loads. A quasi-static numerical model was developed to predict the mechanical behaviour of FMLs under three-point bending load.