Hydrothermal Synthesis and Characterization of TiO2-Derived Nanotubes for Biomedical Applications. Issue 8 (2nd August 2016)

• Record Type: Journal Article
• Authors: Eslami, Hossein; Moztarzadeh, Fathollah; Kashi, Tahereh S. Jafarzadeh; Khoshroo, Kimia; Tahriri, Mohammadreza
• Is Part Of: Synthesis and reactivity in inorganic, metal-organic, and nano-metal chemistry. Volume 46:Issue 8(2016)
• Page Start: 1149
• Page End: 1156
• Publication Date: 2016-08-02
• Subjects: TiO2 -- nanotube -- hydrothermal process -- synthesis -- temperature; Inorganic compounds -- Synthesis -- Periodicals; Organic compounds -- Synthesis -- Periodicals; Organometallic compounds -- Synthesis -- Periodicals; Reactivity (Chemistry) -- Periodicals; Nanostructured materials -- Periodicals; 541.39
• DOI: 10.1080/15533174.2014.988828
• Languages: English
• ISSNs: 1553-3174

Abstract

Abstract : In this research, TiO2 -derived nanotubes were obtained when TiO2 nanopowders were treated chemically with NaOH aqueous solution at various reaction temperatures and subsequently, washing with HCl aqueous solution. While increasing temperature, the morphology altered from spherical particles to sheets at 90°C and then to nanotubes when temperature became higher. Therefore, the reaction temperature is a key factor in elucidating the aspect ratio of tubes, whereby specific surface area varied from 66 m 2 /g for TiO2 nanopowders and reached 337 m 2 /g for synthesized nanotube at 150°C that are expected to have great potentials for biomedical applications. Also, X-ray diffraction results clearly showed the conversion particle to tube of including Na2 Ti3 O7 phase. Electron microscopy micrographs presented the needle-shaped materials with a tubular structure, less than 50 nm in diameter and with length of few hundred nanometers, as well as scroll-like structure and multilayered. Eventually, the 1D prepared structures displayed a remarkable stability during heating and remaining composition even up to 600°C.