Wear particle release at the interface of dental implant components: Effects of different material combinations. An in vitro study. Issue 3 (March 2022)

• Record Type: Journal Article
• Authors: Olander, Julia; Ruud, Amund; Wennerberg, Ann; Stenport, Victoria Franke
• Is Part Of: Dental materials. Volume 38:Issue 3(2022)
• Page Start: 508
• Page End: 516
• Publication Date: 2022-03
• Subjects: Dental implant -- Ceramics -- Abutments -- Dynamical loading test -- Titanium -- Zirconia; Dentistry -- Periodicals; Dental materials -- Periodicals; 617.695
• DOI: 10.1016/j.dental.2022.01.001
• Languages: English
• ISSNs: 0109-5641

Abstract

Highlights: Dynamical loading on dental implants generates particle production and wear. Large particles are trapped inside the internal connection. Particle size is affected by implant and abutment material. Stiffness of the complex is related to type of abutment material. Low level ion release/leakage is seen during corrosion tests. Abstract: Objectives: Particle generation from implant components caused by frictional wear affect the surrounding peri-implant tissues. The objective of this study was to evaluate the effect of combining implant and abutment materials on wear and particle release in a dynamical loading setup. Methods: A customized dynamical loading machine was used to subject two implant materials (Titanium and Titanium- Zirconium alloy) paired with two different abutment materials (Titanium and Zirconia) to a cyclic loading set of 240.000 cycles (simulating 1 year of clinical use). The implant and abutment complex was immersed in corrosive liquid to collect particle debris and measure the release of corroded ions. Scanning electron microscopy was used to analyze signs of wear on the components after testing and evaluate the size and composition of particle debris. Results: Wear signs were evident in all material couplings. Particle debris was found on top, inside the implants, and on the abutment heads. The particle size ranged between 0.6 and 16.9 µm, with larger particles composed of Ti. Smaller-sized particles were found in the container liquid ranging from 0.253 to 1.7 µm compared to inside the implants ranging from 3.25 to 95.3 µm. Larger particles were found inside Tizr implants compared to Ti implants. Low levels of ions released due to corrosion were found when measuring content in surrounding liquid. Significance: Particle generation is evident when subjecting dental implant and abutment couplings in a dynamic loading setup. Internally connected implants hinder the release of larger particles to surrounding container liquid.