High-rate supercapacitive performance of GO/r-GO electrodes interfaced with plastic-crystal-based flexible gel polymer electrolyte. (10th November 2015) - Suleman, Mohd.
Abstract: We report the performance of symmetrical electric double layer capacitors (EDLCs) fabricated with graphene oxide (GO) and reduced graphene oxide (r-GO) electrodes, and plastic crystal based flexible gel polymer electrolyte (GPE) film. The GPE, comprising the solution of lithium bis(trifluoromethanesulfonyl) imide (LiTFSI) in a plastic crystal succinonitrile (SN) entrapped in poly (vinylidinefluoride-co-hexafluoropropylene) (PVdF-HFP), shows suitability as separator/electrolyte in EDLCs due to its excellent electrochemical properties including high ionic conductivity (∼1.97 × 10 −3 S cm −1 a 20 °C). The GO and r-GO electrodes exhibit supercapacitive properties with the SN-based GPE as evidenced from electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV) and galvanostatic charge-discharge analyses. The residual oxygen functionalities associated with GO-electrodes provide additional pseudo-capacitance resulting in higher specific capacitance and specific energy (∼66 F g −1 and 18 Wh kg −1, respectively) as compared to r-GO electrodes (specific capacitance ∼60 F g −1 and specific energy ∼15.6 Wh kg −1 ). High knee frequency fk (∼38 Hz), low response time ∼τ0 (∼166.5 ms) and high pulse power P0 (∼32.9 kW kg −1 ), observed from EIS studies, indicate the high rate capability of GO-electrodes-based EDLCs. About three fold increase in fk and three times decrease in τ0 indicates a substantially higher rate performance of r-GO-based EDLCs with respect to GO-based cell. The high rate capability of GO/r-GO electrodes in combination with SN-based GPEs is further confirmed from the rectangular CV shapes up to scan rates of 5 V s −1 for GO and 10 V s −1 for r-GO electrodes. The r-GO based EDLC offers higher specific power (∼54.9 kW kg −1 ) as compared to that of GO-based EDLC (∼33.3 kW kg −1 ), as observed from charge-discaharge studies. Both EDLCs show stable capacitive performance up to ∼11000-13500 charge-discharge cycles.