Effect of Mg substitution on crystalline structure and hydrogenation of Gd4MgNi19. (18th January 2018)

• Record Type: Journal Article
• Authors: Iwase, Kenji; Terashita, Naoyoshi; Mori, Kazuhiro; Tashiro, Suguru; Suzuki, Tetsuya
• Is Part Of: International journal of hydrogen energy. Volume 43:Number 3(2018)
• Page Start: 1675
• Page End: 1680
• Publication Date: 2018-01-18
• Subjects: XRD -- Rietveld refinement -- Crystal structure -- Superlattice structure -- P-C isotherm; Hydrogen as fuel -- Periodicals; Hydrogène (Combustible) -- Périodiques; Hydrogen as fuel; Periodicals; 665.81
• DOI: 10.1016/j.ijhydene.2017.11.166
• Languages: English
• ISSNs: 0360-3199

Abstract

Abstract: The effect of Mg substitution on Gd4 MgNi19 was investigated using X-ray diffraction (XRD) and pressure-composition (P-C) isotherm measurements. Gd4 MgNi19 consists of 56% Gd2 Co7 -type, 27% Ce5 Co19 -type, and 17% CaCu5 -type structures, which are retained in the hydride phase. Peak broadening was observed in the XRD profile of the hydride phase, while the degree of peak broadening decreased in the hydrogen-desorbed alloy after the P-C isotherm measurement. The reversible hydrogen capacity reached 1.0 H/M. There was a wide plateau region between 0.10 H/M and 0.80 H/M during the absorption-desorption process. Gd5 Ni19 consists of 89% Sm5 Co19 -type and 11% CaCu5 -type structures. After the P-C isotherm measurement, the hydrogen-desorbed Gd5 Ni19 alloy showed severe −peak broadening in the XRD profile. The reversible hydrogen capacity was 0.80 H/M, and there was a sloping plateau in the P-C isotherm. Mg substitution decreases the severe peak broadening and lattice strain after the P-C isotherm measurement, and enhances the hydrogenation property. Highlights: The reversible hydrogen capacity of Gd4 MgNi19 reached 1.0 H/M. The Gd4 MgNi19 consisted of 56% Gd2 Co7 -type, 27% Ce5 Co19 -type and 17% CaCu5 -type phases. The Gd4 MgNi19 alloy is superior in reversible behavior of crystal lattice during hydrogenation.